Surface Modification of Diesel Fuel Equipment Parts Made of KhVG Steel by Saturation with Nitrogen and Carbon to Increase Hardness and Wear Resistance
https://doi.org/10.21869/2223-1528-2021-11-4-22-37
Abstract
Purpose. Show that nitrocarburizing of KhVG steel in a highly active environment significantly increases its hardness and wear resistance due to surface modification with a large amount of carbonitrides.
Methods. For research in an induction furnace, samples with a diameter of 50 m, 8 pieces of steel KHVG, were subjected to nitrocarburizing in a highly active nitrogen-carbon medium, which would provide saturation of the surface layers of steel with carbonitrides of iron alloys with manganese and chromium.
Results. Investigation of the microstructure of modified samples from steel KhVG showed that in all modes of nitrocarburizing, a large amount of a new phase was formed in their surface layers. Inclusions of a new phase in the structure of nitrocarburized layers, as shown by the results of X-ray diffraction analysis, are carbonitrides isomorphic with cementol. The sizes of these carbonitrides vary in the range 3… 10 µm, and the microhardness - in the range Hµ 9150… 10500 MPa. The content of carbonitrides in the modified layers depends on both the temperature and the duration of nitrocarburizing.
Conclusion. The presence of carbonitride inclusions in nitrocarburized layers on the surface of parts leads to a significant increase in their hardness and wear resistance. For practical purposes, it is possible to recommend the content of carbonitrides in modified layers on the surface of parts of 50 ... 60%.
About the Authors
S. A. Grashkov
Kursk State Agricultural Academy named after I. I. Ivanov
Russian Federation
Russian Federation
Sergey A. Grashkov, Cand. of Sci. (Engineering), Associate Professor, Associate Professor of the Department of Processes and Machines in Agricultural Engineering
70 K. Marx str., Kursk 305021
V. I. Kolmykov
Southwest State University
Russian Federation
Russian Federation
Valery I. Kolmykov, Dr. of Sci. (Engineering), Professor, Professor of the Department of Materials Technology and Transport
50 Let Oktyabrya str. 94, Kursk 305040
References
1. Aliev A. A., Ampilogov A. Yu., Aliev A. A. Tsementatsiya i nitrotsementatsiya avtotraktornykh detalei v kipyashchem sloe [Cementation and nitrocarburizing of automotive parts in a fluidized bed]. Metallovedenie i termicheskaya obrabotka metallov = Metallurgy and heat treatment of metals, 2009, no. 4 (646), рр. 31–33.
2. Barabash M. A., Kolmykov D. V., Goncharov A. N., Kolmykov V. I. Povyshenie iznosostoikosti vosstanovlennykh detalei tsementatsiei pri remonte mashin [Increasing the wear resistance of restored parts by cementation during machine repair]. Uprochnyayushchie tekhnologii i pokrytiya = Hardening technologies and coatings, 2009, no. 5 (53), рр. 44–47.
3. Alekhin Yu. G., Grashkov S. A., Ugrimov A. S. [Quality of weld coated plowshares]. Kachestvo v proizvodstvennykh i sotsial'no-ekonomicheskikh sistemakh. Sbornik nauchnykh trudov 5-i Mezhdunarodnoi nauchno-tekhnicheskoi konferentsii [Quality in production and socio-economic systems. Collection of scientific papers of the 5th International Scientific and Technical Conference]; ed. by E. V. Pavlov. Kursk, Universitetskaya kniga Publ., 2017, рр. 11–13. (In Russ.)
4. Alekhin Yu. G., Grashkov S. A., Ugrimov A. S. [Innovative technology for the resto-ration of worn-out parts of automotive vehicles by using electrospark coatings based on electroerosive nanomaterials]. Progressivnye tekhnologii i protsessy. Sbornik nauchnykh statei 3-i Mezhdunarodnoi molodezhnoi nauchno-prakticheskoi konferentsii [Progressive technologies and processes. Collection of scientific articles of the 3rd International Youth Scientific and Practical Conference]; ed. by A. A. Gorokhov. Kursk, Universitetskaya kniga Publ., 2016, рр. 14–17. (In Russ.)
5. Belan E. A., Grashkov S. A., Alekhin Yu. G. [Indicators of quality and technical level of restoration of crankshafts]. Perspektivnoe razvitie nauki, tekhniki i tekhnologii. Sbornik nauchnykh statei 6-i Mezhdunarodnoi nauchno-prakticheskoi konferentsii [Perspective development of science, engineering and technologies. Сollection of scientific articles materials of the 6th International Scientific and Practical Conference]. Kursk, Universitetskaya kniga Publ., 2016, рр. 22–26. (In Russ.)
6. Ageev E. V., Latypova G. R., Davydov A. A., Ageeva E. V. Provedenie rentgeno- spektral'nogo mikroanaliza tverdosplavnykh elektroerozionnykh poroshkov [X-ray spectral microanalysis of hard-alloy electroerosive powders]. Izvestiya Yugo-Zapadnogo gosudarstvennogo universiteta = Proceedings of the Southwest State University, 2012, no. 5 (44), pt. 2, рр. 99–102.
7. Ageev E. V., Latypova G. R., Davydov A. A., Ageeva E. V. Otsenka effektivnosti primeneniya tverdosplavnykh elektroerozionnykh poroshkov v kachestve elektrodnogo materiala [Evaluation of the efficiency of using hard-alloy electroerosive powders as an electrode material]. Izvestiya Yugo-Zapadnogo gosudarstvennogo universiteta. Seriya: Tekhnika i tekhnologii = Proceedings of the Southwest State University. Series: Engineering and Technologies. 2012, no. 1, рр. 19–22.
8. Ageev E. V., Gadalov V. N., Ageeva E. V., Bobryshev R. V. Poroshki, poluchennye elektroerozionnym dispergirovaniem otkhodov tverdykh splavov – perspektivnyi material dlya vosstanovleniya detalei avtotraktornoi tekhniki [Powders obtained by electroerosive dispersion of hard alloys wastes - a promising material for the restoration of parts of automotive equipment]. Izvestiya Yugo-Zapadnogo gosudarstvennogo universiteta = Proceedings of the Southwest State University, 2012, no. 1 (40), pt. 1, рр. 182–189.
9. Ageev E. V., Semenikhin B. A., Ageeva E. V., Latypov R. A. Issledovanie khimicheskogo sostava poroshkov, poluchennykh elektroerozionnym dispergirovaniem tverdogo splava [Investigation of the chemical composition of powders obtained by electroerosive dispersion of hard alloy]. Izvestiya Yugo-Zapadnogo gosudarstvennogo universiteta = Proce- edings of the Southwest State University, 2011, no. 5 (38), pt. 1, рр. 138a–144.
10. Ageeva E. V., Latypov R. A., Burak P. I., Ageev E. V. Poluchenie tverdosplavnykh izdelii kholodnym izostaticheskim pressovaniem elektroerozionnykh poroshkov i ikh issledovanie [Obtaining hard-alloy products by cold isostatic pressing of electroerosive powders and their research]. Izvestiya Yugo-Zapadnogo gosudarstvennogo universiteta = Proceedings of the Southwest State University, 2013, no. 5 (50), рр. 116–125.
11. Blinkov B. S., Kalutsky E. S., Grashkov S. A., Stepashov R. V. [On the issue of deposition of an electrolytic alloy iron-cobalt]. Aktual'nye problemy i innovatsionnaya deyatel'nost' v agropromyshlennom proizvodstve. Materialy Mezhdunarodnoi nauchno-prakticheskoi konferentsii [Actual problems and innovative activities in agricultural production: materials of the International Scientific and Practical Conference]. Kursk, Kursk St. Agricultural Acad. named after I. I. Ivanova Publ., 2015, рр. 55–57. (In Russ.)
12. Grashkov S. A., Pivovar N. A., Alekhin Yu. G. [Influence of the paste-like carburizing agent composition on the carburizing of low-alloy steel KhVG]. Innovatsionnye tendentsii razvitiya rossiiskoi nauki. Materialy XI Mezhdunarodnoi nauchno-prakticheskoi konferentsii molodykh uchenykh [Innovative trends in the development of Russian science]. [materials of the XI International Scientific and Practical Conference of Young Scientists]. Krasnoyarsk, Krasnoyarsk St. Agrarian Univ. Publ., 2018, рр. 170–171.
13. Ageev E. V., Shcherbakov A. V., Alekhin Yu. G., Grashkov S. A. Povyshenie informativnosti protsessa diagnostirovaniya dvigatelei avtomobilei za schet tekhnicheskoi endoskopii [Increasing the information content of the process of diagnosing car engines due to technical endoscopy]. Izvestiya Yugo-Zapadnogo gosudarstvennogo universiteta = Proce- edings of the Southwest State University, 2018, no. 1 (76), pp. 18–26.
14. Goryainov V. V., Eskov D. I. [Strengthening of machine parts by low-temperature chemical-thermal treatment]. Aktual'nye problemy inzhenerno-tekhnicheskogo obespecheniya APK. Materialy Mezhdunarodnoi nauchno-prakticheskoi konferentsii [Actual problems of engineering and technical support of AIC. Materials of the International Scientific and Practical Conference]. Kursk St. Agricultural Academy named after I. I. Ivanova Publ., 2013, рр. 18– 22. (In Russ.)
15. Komarov A. O., Belkin P. N. Vliyanie poverkhnostno-aktivnykh veshchestv na kharakteristiki anodnoi tsementatsii konstruktsionnykh stalei [Influence of surfactants on the characteristics of anodic carburizing of structural steels]. Izvestiya vysshikh uchebnykh zavedenii. Poroshkovaya metallurgiya i funktsional'nye pokrytiya= Proceedings of higher Educational Institutions. Powder Metallurgy and Functional Coatings, 2008, no. 2, рр. 46–49.
16. Kulinskiy A. D., Popov A. V. Kontrol' kachestva tsementatsii detalei metallorezhushchikh stankov s pomoshch'yu raspredelenii skachkov namagnichennosti po polyam starta [Quality control of carburizing parts of metal-cutting machine tools using the distributions of magnetization jumps over the start fields]. Vestnik Rostovskogo gosudarstvennogo universiteta putei soobshcheniya = Proceedings of Rostov State Transport University, 2006, no. 4 (24), рр. 21–25.
17. Mordovin A. I., Fomina L. P., Smirnov A. E., Ryzhov N. M. Analiz effektivnosti gazovykh sred pri vakuumnoi tsementatsii [Analysis of the efficiency of gaseous media during vacuum cementation]. Uprochnyayushchie tekhnologii i pokrytiya = Hardening technologies and coatings, 2008, no. 11 (47), рр. 31–35.
18. Fomina L. P., Fakhurtdinov R. S., Smirnov A. E., Vasiliev V. P., Mordovin A. I. Tsementatsiya i nitpotsementatsiya teplostoikikh stalei v tekhnologicheskoi atmosfepe na osnove azota [Cementation and nitrocarburizing of heat-resistant steels in a technological atmosphere based on nitrogen]. Tekhnologiya mashinostroeniya = Mechanical engineering technology, 2006, no. 11, рр. 14–18.
19. Stepankin I. N., Pozdnyakov E. P. K voprosu vliyaniya predvaritel'noi termicheskoi obrabotki i poverkhnostnogo uprochneniya na strukturu, mikrotverdost' i stoikost' k kontaktnomu iznashivaniyu stali Kh12M, uprochnennoi nizkotemperaturnoi nitrotsementatsiei [To the question of the influence of preliminary heat treatment and surface hardening on the structure, microhardness and resistance to contact wear of steel X12M, hardened by low-temperature nitrocarburizing]. Vestnik Gomel'skogo gosudarstvennogo tekhnicheskogo universiteta im. P. O. Sukhogo = Proceedings of the Gomel State Technical University. O N. Sukhoi, 2016, no. 2 (65), рр. 36–44.
20. Chertov V. М. Osobennosti tsementatsii melkikh detalei [Features of carburizing of small parts]. Tekhnologiya mashinostroeniya = Mechanical engineering technology, 2006, no. 3, рр. 11–13.
Review
For citations:
Grashkov S.A., Kolmykov V.I. Surface Modification of Diesel Fuel Equipment Parts Made of KhVG Steel by Saturation with Nitrogen and Carbon to Increase Hardness and Wear Resistance. Proceedings of the Southwest State University. Series: Engineering and Technology. 2021;11(4):22-37. (In Russ.) https://doi.org/10.21869/2223-1528-2021-11-4-22-37
Views:
143
Email this article 